Diffusion and phase transformation behavior in poly-synthetically-twinned (PST) titanium-aluminum/titanium diffusion couple [electronic resource].

Author/Creator:
Pan, Ling.
Format/Description:
Book
209 p.
Subjects:
Materials science.
Metallurgy.
System Details:
Mode of access: World Wide Web.
Summary:
Motivated by the great potential applications of gamma titanium aluminide based alloys and the important effect of diffusion on the properties of gamma-TiAl/alpha2-Ti3Al two-phase lamellar structure, we conduct this thesis research to explore the microstructural evolution and interdiffusion behavior, and their correlations in multi-phase solid state diffusion couples made up of pure titanium and polysynthetically-twinned (PST) Ti-49.3 at.% Al "single" crystal, in the temperature range of 973--1173 K. The diffusion couples are prepared by high vacuum hot-pressing, with the diffusion direction parallel to the lamellar planes. Scanning electron microscopy (SEM), transmission electron microscopy (TEM) and high-resolution transmission electron microscopy (HRTEM) are employed to observe the microstructure at various interfaces/interphases. A reaction zone (RZ) of polycrystalline alpha 2-Ti3Al phase forms along the PST Ti-Al/Ti bonding interface having a wavy interface with the PST crystal and exhibits deeper penetration in alpha2 lamellae, consisting of many fine alpha2 and secondary gamma laths, than in primary gamma lamellae. Direct measurement of the RZ thickness on SEM back-scattered electron images reveals a parabolic growth of the RZ, indicating a macroscopically diffusion-controlled growth. Concentration profiles from Ti, through the RZ, into the alpha2 lamellae of the PST crystal are measured by quantitative energy-dispersive x-ray spectroscopy (EDS) in a scanning transmission electron microscope (STEM). A plateau of composition adjacent to the RZ/(mixed alpha2 lath in PST) interface forms in the deeply penetrated RZ grains, implying a diffusion barrier crossing the interface and some extent of interface control in the RZ grain growth. The interdiffusion coefficient is evaluated both independent of composition and as a function of composition. No significant concentration dependence of the interdiffusion coefficients is observed using Boltzmann-Matano analysis. The temperature dependence of the interdiffusion coefficients obeys the Arrhenius relationship with a pre-exponential factor of D 0 = (7.56 +/- 7.14) x 10-5 m2/s and an activation enthalpy of Q = 255.6+8.9-8.3 kJ/mol = (2.65 +/- 0.09) eV/atom. The initial nucleation stage of the RZ grains plays an important role in the later microstructural evolution as does the local mass balance. The interfacial energy and the strain energy in the deeply penetrated RZ grains are possible reasons for the plateau.
Notes:
Source: Dissertation Abstracts International, Volume: 63-11, Section: B, page: 5458.
Supervisor: David E. Luzzi.
Thesis (Ph.D.)--University of Pennsylvania, 2002.
Local notes:
School code: 0175.
Contributor:
University of Pennsylvania.
Contained In:
Dissertation Abstracts International 63-11B.
ISBN:
9780493929316
Access Restriction:
Restricted for use by site license.
Location Notes Your Loan Policy
Description Status Barcode Your Loan Policy